DuPont Performance Polymers Delrin? 111P NC010 Acetal Homopolymer
Polymer,Thermoplastic,Acetal (POM)
DuPont Performance Polymers
產品說明:
Delrin? 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and modulus than Delrin? 100P.
Information provided by DuPont Performance Polymers
DuPont Performance Polymers Delrin? 111P NC010 Acetal Homopolymer 物性表
| 物理性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 比重 | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| 密度 | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 |
| Water Absorption | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Immersion 24h; ASTM D570 |
| 1.0 % @Temperature 23.0 °C | 1.0 % @Temperature 73.4 °F | Saturation, immersed; ISO 62, Similar to | |
| 線性成型收縮率 | 0.017 - 0.020 cm/cm @Thickness 3.20 mm | 0.017 - 0.020 in/in @Thickness 0.126 in | Transverse, 24h; ASTM D955 |
| 0.018 - 0.021 cm/cm @Thickness 3.20 mm | 0.018 - 0.021 in/in @Thickness 0.126 in | Flow, 24h; ASTM D955 | |
| 線性模具收縮，Flow | 0.018 - 0.021 cm/cm @Thickness 4.00 mm | 0.018 - 0.021 in/in @Thickness 0.157 in | Parallel, 24h; ISO 294-4 |
| 0.021 cm/cm @Thickness 2.00 mm | 0.021 in/in @Thickness 0.0787 in | ISO 294-4 | |
| 線性成型收縮率,橫向 | 0.019 cm/cm @Thickness 2.00 mm | 0.019 in/in @Thickness 0.0787 in | ISO 294-4 |
| 0.018 - 0.021 cm/cm @Thickness 4.00 mm | 0.018 - 0.021 in/in @Thickness 0.157 in | Normal, 24h; ISO 294-4 | |
| 熔體流動速率 | 1.0 g/10 min @Load 1.05 kg, Temperature 190 °C | 1.0 g/10 min @Load 2.31 lb, Temperature 374 °F | ASTM D1238 |
| 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | |
| 化合物熔體指數 | 1.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 374 °F | cm3/10 min; ISO 1133 |
| 機械性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 洛氏硬度（M 級） | 92 | 92 | ISO 2039/2 |
| 洛氏硬度（R 級） | 120 | 120 | ISO 2039/2 |
| 121 | 121 | ASTM D785 | |
| 抗張強度 | 72.0 MPa @Temperature 23.0 °C | 10400 psi @Temperature 73.4 °F | 5mm/min (0.2in/min); ASTM D638 |
| 60.799 MPa @Strain 2.8574 %, Temperature -40.0 °C | 8818.2 psi @Strain 2.8574 %, Temperature -40.0 °F | ISO 527 | |
| 87.176 MPa @Strain 5.7149 %, Temperature -40.0 °C | 12644 psi @Strain 5.7149 %, Temperature -40.0 °F | ISO 527 | |
| 94.877 MPa @Strain 8.5723 %, Temperature -40.0 °C | 13761 psi @Strain 8.5723 %, Temperature -40.0 °F | ISO 527 | |
| 96.84 MPa @Strain 11.43 %, Temperature -40.0 °C | 14050 psi @Strain 11.43 %, Temperature -40.0 °F | ISO 527 | |
| 97.432 MPa @Strain 14.287 %, Temperature -40.0 °C | 14131 psi @Strain 14.287 %, Temperature -40.0 °F | ISO 527 | |
| 97.672 MPa @Strain 17.145 %, Temperature -40.0 °C | 14166 psi @Strain 17.145 %, Temperature -40.0 °F | ISO 527 | |
| 98.055 MPa @Strain 20.002 %, Temperature -40.0 °C | 14222 psi @Strain 20.002 %, Temperature -40.0 °F | ISO 527 | |
| 98.733 MPa @Strain 22.86 %, Temperature -40.0 °C | 14320 psi @Strain 22.86 %, Temperature -40.0 °F | ISO 527 | |
| 99.053 MPa @Strain 25.717 %, Temperature -40.0 °C | 14366 psi @Strain 25.717 %, Temperature -40.0 °F | ISO 527 | |
| 99.549 MPa @Strain 28.574 %, Temperature -40.0 °C | 14438 psi @Strain 28.574 %, Temperature -40.0 °F | ISO 527 | |
| 抗張強度(屈服) | 72.0 MPa @Temperature 23.0 °C | 10400 psi @Temperature 73.4 °F | 5mm/min (0.2in/min); ASTM D638 |
| 72.0 MPa @Temperature 23.0 °C | 10400 psi @Temperature 73.4 °F | ISO 527 | |
| 伸長率 (斷裂) | 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | nominal; ISO 527 |
| 50 % @Temperature 23.0 °C | 50 % @Temperature 73.4 °F | ISO 527 | |
| 73 % @Temperature 23.0 °C | 73 % @Temperature 73.4 °F | 5mm/min (0.2in/min); ASTM D638 | |
| Elongation at Yield | 20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | ISO 527 |
| 21 % @Temperature 23.0 °C | 21 % @Temperature 73.4 °F | 5mm/min (0.2in/min); ASTM D638 | |
| 拉伸模量 | 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | 5mm/min (0.2in/min); ASTM D638 |
| 3.20 GPa @Temperature 23.0 °C | 464 ksi @Temperature 73.4 °F | ISO 527 | |
| 彎曲強度 | 80.0 MPa @Strain 3.50 %, Temperature 23.0 °C | 11600 psi @Strain 3.50 %, Temperature 73.4 °F | ISO 178 |
| 92.0 MPa @Strain 5.00 %, Temperature 23.0 °C | 13300 psi @Strain 5.00 %, Temperature 73.4 °F | ASTM D790 | |
| 彎曲模量 | 2.90 GPa @Temperature 23.0 °C | 421 ksi @Temperature 73.4 °F | ISO 178 |
| 2.97 GPa @Temperature 23.0 °C | 431 ksi @Temperature 73.4 °F | ASTM D790 | |
| 懸壁梁缺口沖擊強度 | 0.960 J/cm @Temperature 23.0 °C | 1.80 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 懸壁梁無缺口沖擊強度 | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D4812 |
| 懸壁梁缺口沖擊強度 | 11.0 kJ/m2 @Temperature -40.0 °C | 5.23 ft-lb/in2 @Temperature -40.0 °F | ISO 180/1A |
| 11.0 kJ/m2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |
| 簡支梁無缺口沖擊強度 | 27.0 J/cm2 @Temperature -30.0 °C | 128 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 30.0 J/cm2 @Temperature 23.0 °C | 143 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| 簡支梁缺口沖擊強度 | 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| 拉伸蠕變模量(1 hr) | 3000 MPa @Temperature 23.0 °C | 435000 psi @Temperature 73.4 °F | ISO 899 |
| 拉伸蠕變模量(1000 hr) | 1700 MPa @Temperature 23.0 °C | 247000 psi @Temperature 73.4 °F | ISO 899 |
| 電氣性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 體積電阻率 | 8.00e+14 ohm-cm @Temperature 23.0 °C | 8.00e+14 ohm-cm @Temperature 73.4 °F | ASTM D257 |
| 表面電阻 | 6.00e+14 ohm @Temperature 23.0 °C | 6.00e+14 ohm @Temperature 73.4 °F | ASTM D257 |
| 介電常數 | 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 |
| 介電強度 | 18.0 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 457 kV/in @Thickness 0.126 in, Temperature 73.4 °F | Short Time; ASTM D149 |
| 耗散因數 | 0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 |
| 相比耐漏電起痕指數(CTI) | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | IEC 60112 |
| 600 V @Thickness 3.00 mm, Temperature 23.0 °C | 600 V @Thickness 0.118 in, Temperature 73.4 °F | UL 746A |
| 熱性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
|---|---|---|---|
| 線形熱膨脹系數 - 流動 | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | ASTM E 831 |
| 500 μm/m-°C @Temperature -40.0 - 23.0 °C | 278 μin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |
| 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |
| 500 μm/m-°C @Temperature 55.0 - 100 °C | 278 μin/in-°F @Temperature 131 - 212 °F | ISO 11359-1/-2 | |
| 線性熱膨脹系數,橫向流動 | 94.0 μm/m-°C @Temperature -40.0 - 23.0 °C | 52.2 μin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 |
| 110 μm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 μin/in-°F @Temperature 73.4 - 131 °F | ASTM E 831 | |
| 110 μm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 μin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 |